Language: 
To browser these website, it's necessary to store cookies on your computer.
The cookies contain no personal information, they are required for program control.
  the storage of cookies while browsing this website, on Login and Register.

GDPR and DSGVO law

Storing Cookies (See : http://ec.europa.eu/ipg/basics/legal/cookies/index_en.htm ) help us to bring you our services at overunity.com . If you use this website and our services you declare yourself okay with using cookies .More Infos here:
https://overunity.com/5553/privacy-policy/
If you do not agree with storing cookies, please LEAVE this website now. From the 25th of May 2018, every existing user has to accept the GDPR agreement at first login. If a user is unwilling to accept the GDPR, he should email us and request to erase his account. Many thanks for your understanding

User Menu

Google Search

Custom Search

Author Topic: Iron remanence question.  (Read 7776 times)

Offline IotaYodi

  • Hero Member
  • *****
  • Posts: 551
Iron remanence question.
« on: November 25, 2009, 05:49:30 PM »
Ive tried to hunt this down but can find anything. Which Iron has the least amount of remanence. Ductile or cast?

Offline blindsangamon

  • Newbie
  • *
  • Posts: 6
Re: Iron remanence question.
« Reply #1 on: July 11, 2011, 10:29:26 PM »
The softer and purer the iron, the lower the remanence.  Annealed iron (heated red hot and allowed to cool slowly) will have very low remanence.  Any carbon or other impurities will increase its remanence.