You are welcome Drannom,

I look forward to hearing the results you get.

My friend is away at work for a few more days. I will ask him for the details of spin again when he returns. I did already, but at the time it was from interested curiosity and I do not remember how fast the vortex moved. - except that it was slow and needed to be filmed in a  stop motion sort of way.

Actually, however, if it is a pyramid that is making the vortex that moves the water, perhaps it will be the exactly right speed to create another one in the solution!

I am always hopeful for easy and excellent results.

Thank you again for sharing your techniques with us. (I love the potential that is in a pyramid!)

jeanna

Hello Jesus, you are a genious ! you have learned almost perfectly what i do

i just want to complete your post

the gravity attract most of the potassium alum dissolved at the bottom of any container, with the vortex propeller we homogenize the solution, then there will be no over saturation at the bottom

for the seed germination, the gravity will do some pressure at the bottom, and more the concentration increase more are the chance to get a micro-burst, each micro-burst will give a crystal, so in the seed germination we need to get the saturation increase slowly with a slowly cooling method

if it is not working then we have to increase or decrease the saturation and try again, and yes the atmospheric pressure is a parametre, and there are too much parametre, we have to let down the scientific method and make some manual calibration of the solution

if we get a slowly cooling then the micro-burst will be stronger, with a micro-burst you can get together 2 molecules, or 3 molecules, or 4 molecules, or more

if 2 molecules cristallized in a micro-burst then they fall down at the bottom of the container and keep going cristallizing with other molecules, it will be the normal form of potassium alum, kind of hexagonal shape

if 3 molecules cristallized in a micro-burst, then it will look like a chair with only 3 legs, the 3 molecules fall down and keep going cristallizing, it will be possibly a pyramid or not, cause the forth leg can cristallize just before the structure touch the bottom of the container

if 4 molecule cristallized in a micro burst, then you get a pyramid

if more than 4 cristallized, then the solution has been cool to fast, or the solution is too concentrate, with 8 you get an octahedron ! very rare

if you get sort of snow on all the bottom's surface, then cooling too fast or solution too concentrate

Jesus you have catch the crystal generator too ! very good

to grow a pyramid with a crystal generator you have to place the crystal generator (or a big seed) in a solution of water and potassium alum just saturated a little bit and a little hot, so the crystal will melt a little bit before growing , again the most difficult part is to calibrate the solution, i do this simply, i use a poor solution with alum in it at room temperature, and i add the part i wish to dissolve, and then when cooling the same part will come back

so, i put the crystal generator or a big seed in the Cristallarium, then it is dissolve a little bit the time of the first cooling (1 hour max), and will begin to cristallize then, after this we have to inject alum from a hot saturated solution (30 celsius) to the Cristallarium (20 celsius), and the difference in those temperature give the right concentration

you can inject with a feeding bottle or a circulating system more complex

the lamp under the foam disk is for 2 purpose, first it is for get the bottom as hot as the top of the solution, even if you use a propeller there will be always a difference between the top and the bottom temperature, second it prevent bad crystal to appear everywhere, cause the glass or ceramique will transmit some cool, sort of lack in infra red rays, in the seed method the glass will give the micro-burst as the cold enter the solution by the bottom, and third the lamp can control the speed of the growing crystal

Hello Jeanna, i have not try the experiment yet, i promise you to try it first tomorrow morning, and i will make a video in slow motion, last year i have put a big pyramid on a floting foam, the pyramid was always moving slowly, i will do it again in my basement to avoid any vibration, my theory is the superlight field is not constant, as the black hole rise and set like a sun in the sky

the center of our galaxy is at aquarius (i think) so it is like a sun rise and a sun set, in fact all planets in our solar system change the field of the superlight

good night









 

I must speak with you ASAP ASAP!!! your Email does not work

We want you hire you to make big Crystals  My email direct
jriddle@genesisplanetsaver.com Time is running out and we
need your help

Jeffrey